“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.
Export
Bošnjak, Branka, 1970-
Uticaj nikla, molibdena i bakra na svojstva austemperovanih nodularnih livova
Autorstvo-Nekomercijalno-Deliti pod istim uslovima 3.0 Srbija (CC BY-NC-SA 3.0)
Academic metadata
Phd. theses
Tehnicko-tehnološke nauke
doktor nauka - metalurško inženjerstvo
Univerzitet Crne Gore
Metalurško-tehnološki fakultet
Studijski program Metalurgija
Other Theses Metadata
Influence of nickel, molybdenum and copper on the characteristic of austempered ductile irons
[B. Bošnjak]
PDF/A (145 listova)
Radulović, Branko, 1970- (mentor)
Perović, Boško, 1929 (član komisije)
Pop Tonev, Kiro (član komisije)
šiđanin, Leposava, 1940- (član komisije)
radmilović, Velimir, 1948- (član komisije)
Austemperovani nodularni livovi (ADI) predstavljaju novu porodicu materijala čija mehanička svojstva zavise od izbora hemijskog sastava i parametara termičkog tretmana. U poslednje vrijeme, značajno se povećao interes za proizvodnjom i razvojem austemperovanih nodulamih livova. Odlična kombinacija čvrstoće, žilavosti loma i otpornosti na habanje omogućava široku primjenu ovih materijala, kako u automobilskoj i željezničkoj, tako i u idustriji teških mašina. Komercijalna upotreba ovih novih materijala konstantno se povećava, a skoro definisanje standarda ASTM A897M: 1990 učiniće njihovu primjenu joć većom.
Eksperimentalni dio ove doktorske disertacije obuhvatio je proizvodnju četiri legirana tipa nodularnog liva, istraživanje uticaja različitih faktora na struktuma i mehanička svojstva, karakteristike loma, prokaljivost, kinetiku procesa i optimalni opseg procesiranja.
Cilj istraživanja u okvim ove doktorske disertacije bio je definisanje korelativnih odnosa između hemijskog sastava legure i parametara termičkog tretmana, sa jedne strane i kinetike procesa, stmktumih i mehaničkih svojstava, sa druge strane.
The term austempered ductile iron (ADI) refers to a new family of materials whose mechanical properties can vary by the correct selection of chemical composition and heat treatment variables. In recent years, there has been significant interest in processing and developing of ADI. Its excellent combination of strength, fracture toughness and wear resistance make ADI suitable for a wide variety of apphcations in automative, rail and heavy engineering industries. The commercial use of this new family of irons is continualIy increasing and the recent establishment of standards such as ASTM A897M:1990 will encourage further applications.
Experimental part of this dissertation included production of four alloyed ductile irons, investigation of different influential parameters on structural and mechanical properties, characteristic of fracture, austemperabihty, ausiempering kinetic and processing windows.
The aim of investigation in this dissertation was determination of relations of alloy chemical composition and parameters of austempering, on one hand and austempering kinetic, structural and mechanical properties on other hand.
Austemperovani nodularni livovi (ADI) predstavljaju novu porodicu materijala čija mehanička svojstva zavise od izbora hemijskog sastava i parametara termičkog tretmana. U poslednje vrijeme, značajno se povećao interes za proizvodnjom i razvojem austemperovanih nodulamih livova. Odlična kombinacija čvrstoće, žilavosti loma i otpornosti na habanje omogućava široku primjenu ovih materijala, kako u automobilskoj i željezničkoj, tako i u idustriji teških mašina. Komercijalna upotreba ovih novih materijala konstantno se povećava, a skoro definisanje standarda ASTM A897M: 1990 učiniće njihovu primjenu joć većom.
Eksperimentalni dio ove doktorske disertacije obuhvatio je proizvodnju četiri legirana tipa nodularnog liva, istraživanje uticaja različitih faktora na struktuma i mehanička svojstva, karakteristike loma, prokaljivost, kinetiku procesa i optimalni opseg procesiranja.
Cilj istraživanja u okvim ove doktorske disertacije bio je definisanje korelativnih odnosa između hemijskog sastava legure i parametara termičkog tretmana, sa jedne strane i kinetike procesa, stmktumih i mehaničkih svojstava, sa druge strane.